Synthesis of photoconductive polymer of poly(4 - Diphenylamino styrene) for photorefractive materials

The typical synthesis procedure for the monomer of N,N-diphenyl-4-vinylaniline was conducted and has been proved to be ineffective in the university laboratory conditions. The modified procedure was applied successfully using freshly formed Wittig reagent. The monomer was characterized by proton nuclear magnetic resonance (1H NMR) spectroscopy and confirmed the chemical structure with the correct peaks. The photoconductive polymer of poly((4- diphenylamino styrene)) could be obtained only by using the white crystal monomer. | TRƯỜNG ĐẠI HỌC SƯ PHẠM TP HỒ CHÍ MINH TẠP CHÍ KHOA HỌC HO CHI MINH CITY UNIVERSITY OF EDUCATION JOURNAL OF SCIENCE ISSN: KHOA HỌC TỰ NHIÊN VÀ CÔNG NGHỆ NATURAL SCIENCES AND TECHNOLOGY 1859-3100 Tập 14, Số 3 (2017): 18-27 Vol. 14, No. 3 (2017): 18-27 Email: tapchikhoahoc@; Website: SYNTHESIS OF PHOTOCONDUCTIVE POLYMER OF POLY(4-DIPHENYLAMINO STYRENE) FOR PHOTOREFRACTIVE MATERIALS Nguyen Huu Vinh1, Nguyen The Manh 1, Nguyen Thi Thuy Hong1, Bach Long Giang1, Giang Ngoc Ha 1,2* 1 2 NTT Institute of Hi-Technology, Nguyen Tat Thanh University Chemical Engineering Faculty, Ho Chi Minh city University of Food Industry Received: 26/9/2016 Revised: 02/32017; Accepted: 24/3/2017 ABSTRACT The typical synthesis procedure for the monomer of N,N-diphenyl-4-vinylaniline was conducted and has been proved to be ineffective in the university laboratory conditions. The modified procedure was applied successfully using freshly formed Wittig reagent. The monomer was characterized by proton nuclear magnetic resonance (1H NMR) spectroscopy and confirmed the chemical structure with the correct peaks. The photoconductive polymer of poly((4diphenylamino styrene)) could be obtained only by using the white crystal monomer. Keywords: Wittig reaction, triphenylamine, synthesis, photoconductive polymer. TÓM TẮT Tổng hợp polymer quang dẫn poly(4-diphenylamino styrene) cho vật liệu quang phi tuyến Phương pháp truyền thống để tổng hợp monomer N,N-diphenyl-4-vinylaniline đã được tiến hành và chứng minh là không hiệu quả trong điều kiện phòng thí nghiệm. Quy trình cải tiến đã được áp dụng thành công sử dụng tác nhân Wittig vừa được hình thành. Cấu trúc hóa học của monomer được phân tích bằng phổ cộng hưởng từ hạt nhân proton và xác nhận sản phẩm với các đỉnh đặc trưng. Polymer quang dẫn poly((4-diphenylamino styrene)) chỉ có thể được tổng hợp với monomer tinh thể màu trắng. Từ khóa: phản ứng Wittig, Triphenylamine, tổng hợp, Polymer quang .