A laboratory study is performed to evaluate the influence of elevated temperature on the strength and microstructural properties of high strength concretes (HSCs) containing ground pumice (GP), and blend of ground pumice and metakaolin (MK) mixture. Twelve different mixtures of HSCs containing GP and MK were produced, water-to-binder ratio was kept constant as . Hardened concrete specimens were exposed to 250 C, 500 C and 750 C elevated temperatures increased with a heating rate of 5 C/min. Ultrasound pulse velocity (Upv), compressive strength (fc), flexural strength (ffs) and splitting tensile strength (fsts) values of concrete samples were measured on unheated control concrete and after air-cooling period of heated concrete. The crack formation and alterations in the matrix, interface and aggregate of HSCs were examined by X-ray diffraction (XRD), scanning electron microscope (SEM) and polarized light microscope (PLM) analyses. XRD, SEM and PLM analyses have shown that, increasing target temperature result with decrease in mechanical properties . Upv, fc, ffs and fsts values. Elevated temperature also results with crack formation, and increasing target temperature caused more cracks. Alterations in the matrix, interface and aggregate were, also observed by these analyses. The experimental results indicate that concrete made with MK + GP blend together as a replacement of cement in mass basis behaved better than control concrete made with cement only, and concrete containing only GP as a cement replacement. | The influence of elevated temperature on strength and microstructure of high strength concrete containing ground pumice and metakaolin