The (1–x)()–xBaTiO3 (BFMT–BT) lead-free ceramics have been fabricated by using the conventional solid-state reaction method. The phase structure of BFMT−BT investigated with X-ray diffraction shows a single perovskite phase. Although 20% mol of Bi2O3 was added into the raw materials in excess, the evaporation of Bi3+ ions during calcining and sintering processes is from 20 to 30% wt. relative to other elements. The effect of BaTiO3 content on the electrical properties of BFMT−BT ceramic was investigated. |