| Tạp chí phân tích Hóa Lý và Sinh học - Tập 25 Số 1 2020 TỔNG HỢP NGHIÊN CỨU ĐẶC TRƯNG CẤU TRÚC VÀ HOẠT TÍNH QUANG XÚC TÁC PHÂN HỦY METYLEN XANH CỦA HỆ NANO SPINEL ZnxNi1-xFe2O4 x 0 0 5 Đến tòa soạn 20-12-2019 Nguyễn Thị Tố Loan Nguyễn Thị Yến Nguyễn Quang Hải Trường Đại học Sư phạm Thái Nguyên Nguyễn Thị Thúy Hằng Trường Đại học Kỹ thuật Công nghiệp Thái Nguyên SUMMARY PREPARATION CHARACTERIZATION AND PHOTOCATALYTIC ACTIVITY FOR DEGRADATION OF METHYLEN BLUE OF SPINEL ZnxNi1-xFe2O4 x 0-0 5 NANOPARTICLES ZnxNi1-xFe2O4 x 0 nanoparticles have been prepared by a solution combustion method using glycine as fuel. The samples were characterized by X-ray diffraction scanning electron microscopy energy dispersive X-ray spectroscopy. The XRD results showed that the single-phase Zn2 substituted nickel ferrite nanoparticles exhibit partially inverse spinel structure with the crystallite size of 17 21 nm. The morphology of spinel nanoparticles was observed from SEM images and the elemental mapping of Zn-substituted NiFe2O4 was obtained by using energy dispersive X-ray technique. The maximum photocatalytic degradation efficiency for is around when compared to that of NiFe2O4 whose efficiency is around . The improvement in photocatalytic degradation efficiency is due to the effective separation and prevention of electron-hole pair recombination. Keyword Spinel Zn-substituted NiFe2O4 nanoparticles glycine photocatalytic activity methylene blue 1. MỞ ĐẦU từ tính 1-3 . Một số tác giả đã sử dụng chất Trong những năm gần đây với sự phát triển xúc tác ferit trong phản ứng phân hủy nhiều mạnh mẽ của nhiều ngành công nghiệp dệt đã hợp chất hữu cơ như metylen xanh 3 4 và đang làm cho môi trường nước ngày càng bị rhodamin B 5 congo đỏ 6 . Tính chất xúc ô nhiễm bởi các hợp chất hữu cơ. Một trong tác của ferit phụ thuộc vào hình thái học kích những phương pháp hiệu quả để xử lý các chất thước hạt sự thay thế ion trong mạng tinh thể. hữu cơ khó phân hủy là .