Đề tài nêu lên một phương pháp đơn giản cho sự tổng hợp chất hấp phụ hỗn hợp nano oxid mangan-sắt để hấp phụ ion kim loại As(V) từ dung dịch nước. Phương pháp kính hiển vi điện tử truyền qua (TEM), nhiễu xạ tia X (XRD), kính hiển vi điện tử quét (SEM), phổ hồng ngoại (FTIR), phân tích BET được sử dụng để xác định kích thước hạt và đặc trưng của hỗn hợp nano oxid mangan-sắt. Mời các bạn cùng tham khảo! | KỶ YẾU HỘI NGHỊ KHOA HỌC THƯỜNG NIÊN TRƯỜNG ĐẠI HỌC ĐÀ LẠT NĂM 2018 SYNTHESIS AND APPLICATION OF MIXED MANGANESE-IRON OXIDE NANOPARTICLES FOR ADSORPTION OF As V FROM AQUEOUS SOLUTIONS Synthesis of adsorbent and its adsorption Le Ngoc Chunga Le Thanh Quoca a The Faculty of Chemistry Dalat University Lamdong Vietnam Correspoding author Email chungln@ Abstract A simple method has been used to synthesize nanoparticles of mixed manganese-iron oxide for the adsorption of As V metal ions from aqueous solutions. Transmission Electron Microscopy TEM X-Ray diffraction XRD Scanning Electron Microscopy SEM Fourier transform infrared spectroscopy FTIR BET analysis were used to determine particle size and characterization of produced nanoparticles. The x-ray diffraction pattern indicated that the as-synthesized adsorbent is amorphous with m2 g surface area the amorphous synthesized products were aggregated with many nanosized particles. The crystallinity of the Mn2O3 Fe2O3 were obtained at 400 C and 600 C calcination temperature. The FTIR spectra confirmed the presence of -OH group and H-O-H group localized at 3200 - 3400 cm 1 and 1618-1653 cm 1 theses intense bands is weak fade at the high calcination temperature of the mixed manganese-iron oxide nanoparticles. In addition when the calcination temperature of the mixed manganese-iron oxide nanoparticles was 400OC the weak absorption bands at 630 cm 1 due to the vibrations of Fe-O . The results showed that the mixed manganese-iron oxide nanoparticles has high selectivity for As V . Keywords Mixed manganese-iron oxide nanoparticles Amorphous As V . 53 KỶ YẾU HỘI NGHỊ KHOA HỌC THƯỜNG NIÊN TRƯỜNG ĐẠI HỌC ĐÀ LẠT NĂM 2018 TỔNG HỢP VÀ ỨNG DỤNG HỖN HỢP NANO OXID MANGAN- SẮT ĐỂ HẤP PHỤ As V TỪ DUNG DỊCH NƯỚC Tổng hợp chất hấp phụ và tính chất hấp phụ Lê Ngọc Chunga Lê Thành Quốca a Khoa Hóa học Trường Đại học Đà Lạt Lâm Đồng Việt Nam Tác giả liên hệ Email chungln@ Tóm tắt Một phương pháp đơn giản cho sự tổng
