Tuning the mechanical properties and degradation properties of polydioxanone isothermal annealing

Polydioxanone (PPDO) is synthesized by ring-opening polymerization of p-dioxanone, using stannous octoate as the catalyst. The polarized optical micrograph (POM) shows thes pherulite growth rate of PPDO decreases with an increase in the isothermal crystallization temperature. PPDO is compression-molded into bars, and PPDO bars are subjected to isothermal annealing at a range of temperatures (Ta = 50, 60, 70, 80, 90, and 100 °C), and correspond to three different annealing times (ta = 1h, 2h, 3h). The effect on PPDO is investigated by using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), X-ray diffraction (XRD), and scanning electron microscopy (SEM). | Turkish Journal of Chemistry Turk J Chem 2020 44 1430-1444 http chem TÜBİTAK Research Article doi kim-2006-55 Tuning the mechanical properties and degradation properties of polydioxanone isothermal annealing 1 2 1 2 1 1 2 1 2 1 2 1 Xiliang LIU Shaomin FENG Xin WANG Jin QI Dong LEI Yadong LI Wei BAI 1 Chengdu Institute of Organic Chemistry Chinese Academy of Sciences Chengdu . China 2 University of Chinese Academy of Sciences Beijing . China Received Accepted Published Online Final Version Abstract Polydioxanone PPDO is synthesized by ring-opening polymerization of p-dioxanone using stannous octoate as the catalyst. The polarized optical micrograph POM shows thes pherulite growth rate of PPDO decreases with an increase in the isothermal crystallization temperature. PPDO is compression-molded into bars and PPDO bars are subjected to isothermal annealing at a range of temperatures Ta 50 60 70 80 90 and 100 C and correspond to three different annealing times ta 1h 2h 3h . The effect on PPDO is investigated by using differential scanning calorimetry DSC thermogravimetric analysis TGA X-ray diffraction XRD and scanning electron microscopy SEM . With an increase in Ta and ta the grain size and the degree of crystallinity also increase. Meanwhile the tensile strength is significantly improved. The PPDO bars 90 C 2 h reach the maximum crystallinity and the maximum tensile strength MPa . Interestingly the heat treatment process does not result in serious thermal degradation. It is observed that the hydrolytic degradation of the annealed PPDO is delayed to some extent. Thus annealed PPDO might have potential applications particularly in the fields of orthopedic fixation and tissue engineering. Key words Polydioxanone PPDO isothermal annealing mechanical properties hydrolytic degradation in vitro 1. Introduction With the rapid development of agriculture medicine and food packaging people are .

Không thể tạo bản xem trước, hãy bấm tải xuống
TÀI LIỆU XEM NHIỀU
TỪ KHÓA LIÊN QUAN
TÀI LIỆU MỚI ĐĂNG
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.