lectrocatalytic effect of the untreated and TiO2 +polyacrylonitrile (PAN) modified discarded battery coal (DBC) and pencil graphite electrodes (PGE) were evaluated in fuel cell (FC) applications. TiO2+PAN solution is coated on PGE and DBC electrodes by electrospinning. According to the FESEM and EDS characterizations, TiO2 and PAN nanofibers are found to be approximately 40 and 240 nm in size. TiO2+PAN/PGE showed the best FC performances with A cm–2 current density and W cm–2 power density values, whereas TiO2+PAN/DBC showed A cm–2 current density and W cm–2 power density values. |