The results showed that the active component Zr(SO4 )2 was successfully adhered to the mesoporous SiO2 , and the acid amount of Zr(SO4)2/SiO2 increased with the increasing of the Zr(SO4)2 loadings. Finally, the wheat stalk was used as raw material and depolymerized over Zr(SO4)2/SiO2 to produce ethyl levulinate (EL). The reaction mixture was separated and purified by filtration and vacuum distillation. The kinetic characteristics and the reaction pathway were also studied. A comparative study showed that 20 wt.% Zr(SO4)2/SiO2 exhibited higher catalytic activity. When reaction temperature, time, catalyst dosage and Zr(SO4)2 loadings were 190 °C, 50 min, 20 wt.% and 30 wt.%, the EL yield reached a maximum of . The relative content of EL exceeded 90% after three steps of distillation. |