Mesoporous polyethylene glycol (PEG)/silica and carbon black (CB)/silica xerogel composites were prepared by the solgel method as an adsorbent for CO2 adsorption. The CO2 adsorption process was carried out under pure CO2 atmosphere at room temperature in addition to ambient air. The xerogel composites with high surface area and pore volume showed better CO2 adsorption capacity than the pure silica xerogel. After modifying samples with propylene diamine using the wet impregnation method, an increase in CO2 adsorption capacity was observed for the samples except CB/silica xerogel composite. |