Bài viết Cấu trúc, hình thái và tính chất từ trong nano tổ hợp Fe/Fe3O4 báo cáo chi tiết về sự tiến triển của các pha tinh thể, hình thái cũng như tính chất từ của vật liệu tổ hợp Fe/Fe3O4 được ôxy hóa dưới các nhiệt độ khác nhau. | TNU Journal of Science and Technology 227 16 55 - 61 STRUCTURE MORPHOLOGY AND MAGNETIC PROPERTIES IN Fe Fe3O4 NANOCOMPOSITES Do Hung Manh1 Le Thi Hong Phong1 Ta Ngoc Bach1 Nguyen Van Dang2 Nguyen Van Khien2 Ivan Skorvanek3 1 Institute of Materials Science - Vietnam Academy of Science and Technology 2 TNU - University of Sciences 3Slovak Academy of Sciences Kosice Slovakia ARTICLE INFO ABSTRACT Received 06 9 2022 The influence of annealing temperature on the structure morphology and magnetic properties of Fe Fe3O4 nanocomposite powder was Revised 07 10 2022 investigated. The samples were fabricated by combining high-energy Published 10 10 2022 ball milling and annealing at temperatures of 623 723 and 823 K. The structure and morphology of the samples were characterized by X-ray KEYWORDS diffraction scanning electron microscopy. These measurements indicated the evolution of the crystalline phases of the samples as the Fe Fe3O4 nanocomposites temperature increases. At the same time the morphology of the Lamellar structure samples changed abnormally at different annealing temperatures granular 623 K leaf 723 K and rod 823 K . The room-temperature X-ray diffraction magnetization measurements pointed out a decrease of saturation Magnetic properties magnetization as annealing temperature increases while coercivity Verwey phase transition increases. Besides the presence of a Verwey phase transition near 120 K is confirmed the good crystal quality of Fe 3O4 phase. Our study demonstrates the possibility of tuning the morphology and magnetism in iron iron oxide nano systems through controlled oxidation at the different temperatures. CẤU TRÚC HÌNH THÁI VÀ TÍNH CHẤT TỪ TRONG NANO TỔ HỢP Fe Fe3O4 Đỗ Hùng Mạnh1 Lê Thị Hồng Phong1 Tạ Ngọc Bách1 Nguyễn Văn Đăng2 Nguyễn Văn Khiển2 Ivan Skorvanek3 1 Viện Khoa học vật liệu - Viện Hàn lâm Khoa học và Công nghệ Việt Nam 2 Trường Đại học Khoa học - ĐH Thái Nguyên 3Viện Hàn lâm Khoa học Slovakia Kosice Slovakia THÔNG TIN BÀI BÁO TÓM TẮT