Smithells Light Metals Handbook Episode 10

Tham khảo tài liệu 'smithells light metals handbook episode 10', kỹ thuật - công nghệ, cơ khí - chế tạo máy phục vụ nhu cầu học tập, nghiên cứu và làm việc hiệu quả | Heat treatment of light alloys 175 Table continued Material designation Alloy type Temper Solution treatment Ageing temperature C Time at temperature h Temperature C Quench mediumT 2014A Al Cu4 Si Mg T 3 TD 505 5 Water Room 48 T 4 tb 505 5 Water Room 48 T 6 TF 505 5 Water 155-190 5-20 T 651 505 5 Water 155-190 5-20 2024 Al Cu4 Mg1 T 351 495 5 Water Room 48 T 4 TB 495 5 Water Room 48 T 42 495 5 Water Room 48 2031 Al Cu2 Ni1 Mg Te Si T 4 TB 525 10 Water or oil 155-205 2-20 2117 Al Cu2 Mg T 4 tb 495 5 Water Room 96 2618A Al Cu2 Mg15 Te1 Ni1 T 6 TF 530 5 Water 160-200 16-24 6061 Al Mg1 Si Cu T 4 TB 525 15 Water Room T 6 TF 525 15 Water 165-195 3-12 6063 Al Mg Si T 4 TB 525 5 Water Room T 5 TE 160-180 5-15 T 6 TF 525 5 Water 160-180 5-15 6082 Al Si1 Mg Mn T 4 TB 530 10 Water Room 1 20 T 6 TF 530 10 Water 175-185 7-12 T 651 525 15 Water 165-195 3-12 6101A Al Mg Si T 4 TB 525 5 Water Room 1 20 T 6 TF 525 5 Water 170 10 6463 Al Mg Si T 4 TB 525 5 Water Room 1 20 T 6 TF 525 5 Water 170 10 5-15 7010 Al Zn6 Mg2 Cu2 T 351 475 10 Water T 7651 475 10 Water 172 3 6-15 or 120 3 24 followed by 172 3 6-15 T 73651 465 10 Water 172 3 10-24 7014 Al Mg2 Cu Mn T 6 TF 460 10 Water 85 C or oil 135 5 12 T 6510 460 10 Water or oil 135 5 12 7075 Al Zn6 Mg Cu T 6 TF 460 10 Water 135 5 12 T 651 460 10 Water 135 5 12 T 73 465 5 Water 60-80 C 110 5 6-24 or 120 5 20-30 followed by 177 5 6-10 T 7351 465 5 Water 110 5 6-24 followed by 177 5 5-12 T 7352 465 5 Water 70 C 110 5 6-24 or 120 5 20-30 followed by 177 5 6-10 Heating to temperature at not more than 20 C h. T Water below 40 C unless otherwise stated. ÍFor temper designation see Table Table ALUMINIUM ALLOY TEMPER DESIGNATIONS Symbol Condition Casting alloys BS 1490 M TB TB7 TE TF TF7 TS As cast Solution treated and naturally aged Solution treated and stabilized Artificially aged Solution treated and artificially aged Solution treated artificially aged and stabilized Thermally stress relieved continued overleaf 176 Smithells .