Tham khảo tài liệu 'smithells light metals handbook part 4', kỹ thuật - công nghệ, cơ khí - chế tạo máy phục vụ nhu cầu học tập, nghiên cứu và làm việc hiệu quả | Mechanical properties of magnesium and magnesium alloys Table MAGNESIUM AND MAGNESIUM ALLOYS WROUGHT - TYPICAL MECHANICAL PROPERTIES AT ROOM TEMPERATURE Specifications Tension Compression Material Nominal composition Form DTD or BS Air BS Gen. Eng. ASTM Elektron Proof stress MPa UTS MPa Elong. Proof stress MPa Hardness VPN 30 kg Mg Mg Sheet annealed 69 185 4 30-35 Bar extruded - 100 232 6 35-45 Mg-Mn Mn Sheet 118C 3370-MAG-S-101M - AM503 100 232 6 35-45 Extruded bar 1 in diam. 142B 3373-MAG-E-101M M1A-F B107 162 263 7 124 45-55 Extruded tube 737A 3373-MAG-E-101M M1A B107 154 247 6 45-55 Mg-Al-Zn Al Sheet annealed 3370-MAG-S-1110 AZ31 B90 AZ31 131 232 13 50-60 Zn half hard 3370-MAG-S-111M AZ31 B90 170 263 10 100 55-70 Mn Extruded bar and sections 3373-MAG-E-111M AZ31 B107 162 255 11 93 50-60 Al Forgings 2L513 3372-MAG-F-121M AZ61 B91 AZM 183 293 8 147 60-70 Zn Extruded bar and sections 2L512 3373-MAG-E-121N AZ61 B107 183 293 8 147 55-70 Mn Extruded tube 2L503 3373-MAG-E-121M AZ61 B107 170 278 8 147 60-70 Al Zn Mn Forgings 88C - AZ80A B91 AZ855 208 293 8 185 65-75 Mg-Zn-Mn Zn Sheet annealed 5091 3370-MAG-S-1310 ZM21 131 232 13 Mn half breed 5101 3370-MAG-S-131M 170 263 10 Extruded bar sections - 3373-MAG-E-131M 162 255 11 Mg-Zn-Zr Zn Sheet 2L514 3370-MAG-S-141M - ZW1 178 263 10 154 55-70 Zr Extruded bar and sections 2L508 3373-MAG-E-141M 208 293 13 177 60-75 Extruded tube 2L509 3373-MAG-E-141M - 193 278 7 60-75 Zn Sheet 2L504 3370-MAG-S-151M - ZW3 185 270 8 154 60-70 40 Smithells Light Metals Handbook Zr Forgings 2L514 3372-NAG-F-151M 224 309 8 193 60-80 Extruded bar and sections 1 in diam. 2L505 3373-MAG-E-151M - 239 309 18 213 65-75 Zn Bars and sections Zr Heat treated 5041A 3373-MAG-E-161TE ZK60A-T5 B107-70 ZW6 270 340 10 255 60-80 Mg-Zn-Cu Mn Zn Bars and sections Cu Mn Heat treated - - ZC71-T6 B107 ZC71 340 360 6 - - Mg-Th-Zn-Zr Th Extruded bar and .