Magnetic interactions and spin-wave stiffness constant of In-substituted yttrium iron garnets

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

Magnetization and Curie temperature of the samples were measured with the SQUID and VSM equipments. The non-magnetic indium ions were found to reside at the octahedral sites, leading to an increase of the total magnetization and a decrease in the Curie temperature. Molecular field coefficients Naa, Ndd and Nad were determined by fitting the experimental thermomagnetization curves in the framework of a two-sublattice ferrimagnetic model. |

TÀI LIỆU LIÊN QUAN

Potts model with two competing binary interactions

Phase transition in the 2D XY model with 3-fold nematic interactions

Ebook Atkins’ physical chemistry (8th edition): Part 2

Ebook Fusion physics: Part 2

Dynamic effects of dipolar interactions on the specific loss power of Mn0.7Zn0.3Fe2O4

Probing cellulose–solvent interactions with self-diffusion NMR: Onium hydroxide concentration and co-solvent effects

Magnetic interactions and spin-wave stiffness constant of In-substituted yttrium iron garnets
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.