Tham khảo tài liệu 'composites manufacturing - materials, product, and process engineering part 12', kỹ thuật - công nghệ, cơ khí - chế tạo máy phục vụ nhu cầu học tập, nghiên cứu và làm việc hiệu quả | FIGURE Theoretical and experimental plots of temperature as a function of time at three positions inside a 64-ply composite. The temperature cure cycle is shown in Figure . The cure and bleeder pressures were constant at 586 kPa 85 psi and 101 kPa psi respectively. Reprinted from Loos . and Springer . J. Composite Mater. 17 135 1983. With permission from Technomic Publishing Company. FIGURE The mass loss normal to the tool plate bottom parallel to the tool plate center and the total mass loss top as a function of time for a 64-ply composite. The temperature cure cycle is shown in Figure . The bleeder pressure was constant at 101 kPa psi . The initial resin content was 42 . Reprinted from Loos . and Springer . J. Composite Mater. 17 135 1983. With permission from Technomic Publishing Company Inc. The temperature distributions and resin flows were determined by models using the same cure temperature and pressures as employed during the test. The results of the models are shown as solid lines in Figures to . It is evident from the figures that the calculated and measured temperatures 2002 by CRC Press LLC FIGURE Theoretical and experimental plots of temperature as a function of time at three positions inside a 64-ply composite. The temperature cure cycle is shown in Figure . The cure and bleeder pressures were constant at 586 kPa 85 psi and 101 kPa psi respectively. Reprinted from Loos . and Springer . J. Composite Mater. 17 135 1983. With permission from Technomic Publishing Company. FIGURE The mass loss normal to the tool plate bottom parallel to the tool plate center and the total mass loss top as a function of time for a 64-ply composite. The temperature cure cycle is shown in Figure . The bleeder pressure was constant at 101 kPa psi . The initial resin content was 42 . Reprinted from Loos . and Springer . J. Composite Mater. 17 135 1983. With permission from Technomic .