Superconductivity in U-T alloys (T = Mo, Pt, Pd, Nb, Zr) stabilized in the cubic γ-U structure by splat-cooling technique

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

We succeed to retain the high-temperature (cubic) γ-U phase down to low temperatures in U-T alloys with less required T alloying concentration (T= Mo, Pt, Pd, Nb, Zr) by means of splat-cooling technique with a cooling rate better than 106 K/s. |

TÀI LIỆU LIÊN QUAN

Applications of High Tc Superconductivity Part 1

Applications of High Tc Superconductivity Part 2

Applications of High Tc Superconductivity Part 3

Applications of High Tc Superconductivity Part 4

Applications of High Tc Superconductivity Part 5

Applications of High Tc Superconductivity Part 6

Applications of High Tc Superconductivity Part 7

Applications of High Tc Superconductivity Part 8

Applications of High Tc Superconductivity Part 9

Applications of High Tc Superconductivity Part 10
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.