Nghiên cứu chế tạo vật liệu tự phân hủy trên cơ sở polylactic axit và tinh bột sắn Việt Nam

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

The technological conditions of obtaining the polylactic acid-Vietnamese cassava starch blend on the mix-brabender were investigated. The optimal conditions were: temperature 160o C, reaction time 6 minutes, screw speed 45 r/min., initial material ratio in weight percentage PLA80- PEG10-TB20. Polyethyleneglycol (PEG) as a plasticizer, PN-47 as a distribution agent was used. It showed that the optimal starch content was 20 wt%. Increase in starch content lead to increase in water absorbability and weight loss of the materials. This kind of material is degraded fast in the soil, but had relatively low mechanical property. There need further investigation on this material in order to improve its mechanical property.

TÀI LIỆU LIÊN QUAN
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.