Study on ito thin films prepared by multi-annealing technique

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

The results show that the best ITO films have electrical resistivity of 2.6 × 10-3 Ω.cm and transparency higher than 90 %, which strongly supports to the application of electrode in solar cell, LED or transistor devices from viewpoints of low-cost production and low-energy consumption. | Journal of Science and Technology 54 (1A) (2016) 136-142 STUDY ON ITO THIN FILMS PREPARED BY MULTI-ANNEALING TECHNIQUE Nguyen Quang Hoa1, Nguyen Thi Xuyen1, Vuong Quoc Viet2, Vu Thi Huyen Trang1, Hoang Ha2, Hoang Thi Thanh Tam2, Vu Thi Dung2, Tran Van Dung2 and Bui Nguyen Quoc Trinh2, * 1 Vietnam National University, Hanoi University of Science, Faculty of Physics, 334 Nguyen Trai, Thanh Xuan, Hanoi 2 Vietnam National University, University of Engineering and Technology, Faculty of Engineering Physics and Nanotechnology, 144 Xuan Thuy, Cau Giay, Hanoi * Email: trinhbnq@vnu.edu.vn Received: 31 August 2015; Accepted for publication: 26 October 2015 ABSTRACT Indium tin oxide (ITO) thin films have been successfully prepared by a solution process followed by a multi-annealing method. In this study, we focus on the use of multi-annealing method, for which each layer was annealed at a suitable temperature, instead of a conventional annealing way, by means of a rapid thermal annealing system, in order to improve the film quality. The crystalline structure and surface morphology of the ITO thin films were investigated by using X-ray diffraction (XRD) spectrometer, atomic force microscope (AFM) and scanning electron microscope (SEM). It has been obtained that all of ITO films exhibit a single phase with (222)- and (440)-preferred orientations. The AFM and SEM observations show that the particle size of ITO films was about 10 nm and the ITO film thickness was 180 nm, respectively. In sequence, the electrical properties of ITO thin films were evaluated by using four-point probe and Hall effect measurement methods, and the optical properties were investigated by UV/VIS spectrometer. The results show that the best ITO films have electrical resistivity of 2.6 × 10-3 Ω.cm and transparency higher than 90 %, which strongly supports to the application of electrode in solar cell, LED or transistor devices from viewpoints of low-cost production and .

Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.