Magnetic property of nanoparticle La1–xAxFeO3 (A = Y, Nd) prepared by high - Energy milling method

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

In this paper, the nano perovskite La1–xAxFeO3 sample systems (A = Y, Nd), with x = 0, 0.1, 0.3, were successfully fabricated. The doping of rare earth elements Y or Nd causes the perovskite structure to be distorted, leading to the appearance of a covalent mixed state that strongly affects the of the manufactured materials. The sample system shows the magnetic properties close to the superparamagnetic state at room temperature. |

TÀI LIỆU LIÊN QUAN

Abnormal magnetic property in Fe-doped BaTio3 multiferroics

Magnetic property of nanoparticle La1–xAxFeO3 (A = Y, Nd) prepared by high - Energy milling method

Immobilizing alcalase R enzyme onto magnetic nanoparticles

KxNiy[Fe(CN)6].xH2O prussian blue analogue: A study of size effect on the structural, optical and magnetic propertiecs

Effect of La on the structure and characteristics of multiferroic BiFeO3

Crystal Structure and Magnetic Properties for Bi1-xEuxFeO3 Compounds

Hard magnetic property of Mn-Ga-Al melt-spun ribbons

Magnetic and magnetotransport properties of La0.7Ca0.3Mn1-x(Zn,Cu)xO3

Báo cáo hóa học: " Metal-functionalized single-walled graphitic carbon nitride nanotubes: a first-principles study on magnetic property"

Báo cáo hóa học: " Effects of Proteins from Culture Medium on Surface Property of Silanes- Functionalized Magnetic "
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.