Electrodeposition of Co thin Film onto n-Si(111)/Au substrate

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

Electrodeposition kinetics of Co thin film were investigated and magnetic coercivity of the deposited films were studied using potentiostatic technique and magnetic hyteresis loop measurements. Results showed that the nucleation mechanism of the electrodeposition process changed from instantaneous mode to progressive mode when potential was changed from –0.7 V to –0.8 V. The magnetic coercivity Hc increases with deposition time and the film with Hc < 15 Oe can be obtained with deposition time t < 5 s.

TÀI LIỆU LIÊN QUAN

Facile synthesis of CuO/ITO film via the chronoamperometric electrodeposition for nonenzymatic glucose sensing

Adsorption of Ag+ ions using hydroxyapatite powder and recovery silver by electrodeposition

Electrodeposition of Co thin Film onto n-Si(111)/Au substrate

Electrodeposition of tin(II) from citrate complexes

Báo cáo hóa học: " Gold colloidal nanoparticle electrodeposition on a silicon surface in a uniform electric field"

Báo cáo hóa học: " Over 95% of large-scale length uniformity in template-assisted electrodeposited nanowires by subzero-temperature electrodeposition"

Báo cáo hóa học: " Fabrication of functional micro- and nanoneedle electrodes using a carbon nanotube template and electrodeposition"

Báo cáo hóa học: "Cobalt and Nickel Nanopillars on Aluminium Substrates by Direct Current Electrodeposition Process"

Báo cáo hóa học: " Electrodeposition and Capacitive Behavior of Films for Electrodes of Electrochemical Supercapacitors C. Shi • I. Zhitomirsky

Báo cáo hóa học: " Architectural Growth of Cu Nanoparticles Through Electrodeposition"
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.