Effect of preheating of low shrinking resin composite on intrapulpal temperature and microtensile bond strength to dentin

Không đóng trình duyệt đến khi xuất hiện nút TẢI XUỐNG

The effect of preheating of the silorane-based resin composite on intrapulpal temperature (IPT) and dentin microtensile bond strength (lTBS) was evaluated. For the IPT, teeth (n = 15) were sectioned to obtain discs of 0.5 mm thickness (2 discs/tooth). The discs were divided into three groups (n = 10/group) according to the temperature of the Filtek LS silorane-based resin composite during its placement, either at room temperature (23 ± 1 C) or preheated to 54 C or 68 C using a commercial Calset device. Discs were subjected to a simulated intrapulpal pressure (IPP) and placed inside a specially constructed incubator adjusted at 37 C. | Effect of preheating of low shrinking resin composite on intrapulpal temperature and microtensile bond strength to dentin

TÀI LIỆU LIÊN QUAN

Giáo trình Adobe After Effect

Bài giảng Xử lý kỹ xảo với After Effect: Bài 1

Bài giảng Xử lý kỹ xảo với After Effect: Bài 3

Bài giảng Xử lý kỹ xảo với After Effect: Bài 4

The effect of solvency, firm size, age companies on audit report lag in Indonesian company

Factors affecting customers selection of community pharmacies: The mediating effect of branded pharmacies and the moderating effect of demographics

Work-family enrichment as a mediator effect of supervisor support, self-esteem, and optimism on job satisfaction

The mediating effect of electronic trust in the effect of customer delight to e-loyalty

A study of magnitude of direct and indirect effect relationship in saffron (Croccus sativus L.)

Studies on the effect of nitrogen and potassium on flowering in Crossandra (Crossandra infundibuluformis L.)
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.