Bài viết Ảnh hưởng của nhiệt độ bảo dưỡng mẫu đến sức kháng nứt của bê tông asphalt tái chế nguội đưa ra kết quả nghiên cứu thực nghiệm đánh giá ảnh hưởng của nhiệt độ bảo dưỡng mẫu đến sức kháng nứt của hỗn hợp bê tông asphalt tái chế nguội. | Tạp chí Khoa học Giao thông vận tải Tập 73 Số 3 04 2022 288-299 Transport and Communications Science Journal EFFECT OF TEMPERATURE CURING ON CRACKING RESISTANCE OF COLD RECYCLED ASPHALT MIXTURE Nguyen Ngoc Lan Nguyen Quang Phuc Nguyen Thi Mi Tra Pham Thi Thanh Thuy University of Transport and Communications No 3 Cau Giay Street Hanoi Vietnam ARTICLE INFO TYPE Research Article Received 01 03 2022 Revised 03 04 2022 Accepted 10 04 2022 Published online 15 04 2022 https Corresponding author Email nguyenngoclan@ Tel 84902119278 Abstract. Among the current asphalt concrete technologies the cold recycled asphalt technology with bitumen emulsion and cement can be considered as the lowest energy consumption technology solution because the component materials do not have to be heated during manufacturing. With cold recycled asphalt mixes using bitumen emulsion and cement additives the stiffness of mixture is dependent on curing time and temperature. This paper presents the results of an experimental research to evaluate the effect of curing temperature on the crack resistance of cold recycled asphalt mixture. The results show that the tensile strength failure energy the absolute value of the post-peak slope and the cracking tolerance index increased by and when the sample curing temperature increased from 25oC to 60oC respectively. This result contributes will suggest a appropriate curing temperature to increase the crack resistance of cold recycled asphalt concrete. Keywords Asphalt emulsion Cold recycled Failure energy Cracking tolerance index Tensile strength. 2022 University of Transport and Communications 288 Transport and Communications Science Journal Vol 73 Issue 3 04 2022 288-299 Tạp chí Khoa học Giao thông vận tải ẢNH HƯỞNG CỦA NHIỆT ĐỘ BẢO DƯỠNG MẪU ĐẾN SỨC KHÁNG NỨT CỦA BÊ TÔNG ASPHALT TÁI CHẾ NGUỘI Nguyễn Ngọc Lân Nguyễn Quang Phúc Nguyễn Thị Mi Trà Phạm Thị Thanh Thuỷ Trường Đại học Giao thông vận