Nghiên cứu này trình bày kết quả nghiên cứu chế tạo than sinh học từ bã chưng cất tinh dầu sả theo phương pháp thủy nhiệt, sau đó được hoạt hóa bằng KOH 5M ở nhiệt độ phòng trong 24 h, nghiên cứu các đặc trưng vật liệu và khả năng hấp phụ amoxicillin (AMO) trong môi trường nước. Các đặc trưng vật liệu được xác định bằng các phương pháp nhiễu xạ tia X (XRD), phương pháp phổ hồng ngoại (IR), kính hiển vi điện tử quét (SEM) và phương pháp phân tích bề mặt riêng (BET). | TNU Journal of Science and Technology 228 14 114 - 122 CHARACTERIZATION AND AMOXICILLIN ADSORPTION OF KOH MODIFIED HYDROCHAR FROM DISTILLED WASTE OF LEMONGRASS Truong Thi Thao1 Luong Thi Le Trang1 2 1 TNU - University of Science 2Trang An Secondary School Dong Trieu district Quang Ninh province ARTICLE INFO ABSTRACT Received 11 9 2023 In this study we focused on studying the synthesis of hydrochar from distilled waste of lemongrass by hydrothermal method and then was Revised 17 10 2023 activated by 5 M KOH at room temperature for 24 h TSHS . The TSHS Published 18 10 2023 material was characterized by X-ray diffraction XRD scanning electron microscopy SEM infrared spectroscopy IR and analysis of KEYWORDS specific surface BET . It shows that the TSHS was in the form of amorphous carbon rich in organic functional groups the BET surface Hydrochar area was m2 g. Several factors affecting to the adsorption process of Lemongrass AMO in aqueous media by TSHS were evaluated pH initial AMO concentration the TSHS dosage the adsorption time. The results showed Adsorption that the adsorption was the most effective at pH of 5 adsorption Amoxicillin equilibrium was reached at 3 h the smaller the initial AMO Freundlich isotherm adsorption concentration 5 10 ppm and the higher the TSHS dose g L the adsorption efficiency was about 90 . The experimental adsorption process was consistent with Freundlich isotherm adsorption model and the second-order kinetic model. It means that the adsorption mechanism terminates both physical adsorption and chemical adsorption. ĐẶC TRƯNG VÀ KHẢ NĂNG HẤP PHỤ AMOXICILLIN CỦA THAN SINH HỌC THỦY NHIỆT TỪ BÃ CHƯNG CẤT TINH DẦU SẢ HOẠT HÓA BẰNG KIỀM Trương Thị Thảo1 Lương Thị Lệ Trang1 2 1 Trường Đại học Khoa học - ĐH Thái Nguyên 2Trường THCS Tràng An huyện Đông Triều tỉnh Quảng Ninh THÔNG TIN BÀI BÁO TÓM TẮT Ngày nhận bài 11 9 2023 Nghiên cứu này trình bày kết quả nghiên cứu chế tạo than sinh học từ bã chưng cất tinh dầu sả theo phương pháp .